Aluminum and aluminum alloy surface treatment method
[ Method 1] Degreasing treatment. Wipe with a damp cotton dampening solvent to remove the oil, then wipe it with a clean cotton cloth several times. Commonly used solvents are: trichloroethylene, ethyl acetate, acetone, methyl ethyl ketone and gasoline. Semiconductor Parts,Semiconductor Machine Parts,Cnc Semiconductor Processing Parts,Semiconductor Parts Machining Equipment Shenzhen Kairui Precision Technology Co., Ltd. , https://www.krjgcnc.com
[Method 2] Degreasing solution after the chemical treatment: concentrated sulfuric acid 7.5 water 27.3 weight chromium potassium  65.2 at 60
[Method 3] Degreasing solution after the chemical treatment of: ammonium hydrogen phosphate 20-26 2-2.5 3-3.5 chromium boron concentrated sulfuric acid 0.4-0.6 Water 50-60 25 1000
[ Method 4] Chemical treatment in the following solution after degreasing: phosphoric acid  7.5 chromium oxide 7.5 alcohol 5.0 formaldehyde ( 36-38% ) 80 at 15
[ Method 5] After degreasing, anodizing is carried out in the following solution: concentrated sulfuric acid
[ Method 6] After degreasing, chemical treatment was carried out in the following solution: potassium dichromate 66 sulfuric acid ( 96% ) 666 water  1000 at
[ Method 7] After degreasing, chemical treatment was carried out in the following solution: nitric acid ( d=1.41 ) 3 hydrofluoric acid ( 42% ) 1
[ Method 8] After blasting or sanding, anodizing in the following solution: chromium oxide 100 sulfuric acid 0.2 sodium chloride 0.2 at
[ Method 9] Chemical treatment in the following solution after degreasing: sodium silicate  10 non-ionic detergent 0.1 in
[ Method 10] After degreasing, chemical treatment was carried out in the following solution: sodium fluoride 1 concentrated nitric acid 15 water 84 was immersed at room temperature for 1 min , washed with water and then treated in the following solution: concentrated sulfuric acid 30 dichromate 7.5 water 62.5 at room temperature Dip for 1 min , wash with water and dry.